Effects Of Sn Addition On The Microstructure And Magnetic Properties Of Mnbi Bulk Magnets

JOURNAL OF ALLOYS AND COMPOUNDS(2022)

Cited 2|Views13
No score
Abstract
The Sn addition MnBi bulk magnets with high density and superior coercivity (H-c) were prepared by hot compaction. It was found that the added Sn was dispersed between the MnBi particles as an intergranular phase. The appropriate intergranular phase content could be beneficial in improving the H-c due to the strong magnetic isolation effects. The H-c of the MnBi/Sn bulk magnet was increased from 8.6 kOe to 11.5 kOe as the Sn addition contents were increased in the range of 0 wt.% to 5 wt.%. A relatively high squareness (M-r/M-s) of 0.91 was obtained for the 1 wt.% Sn addition Mn56Bi44 bulk magnet exhibiting the maximum energy product (BH)(max) of 7.8 MGOe with high H-c of 10 kOe at room temperature. (C) 2021 Elsevier B.V. All rights reserved.
More
Translated text
Key words
MnBi bulk magnets, Sn addition, Intergranular phase, Enhanced coercivity
AI Read Science
Must-Reading Tree
Example
Generate MRT to find the research sequence of this paper
Chat Paper
Summary is being generated by the instructions you defined