Berry curvature origin of the thickness-dependent anomalous Hall effect in a ferromagnetic Weyl semimetal

Magnetic Weyl semimetals with spontaneously broken time-reversal symmetry exhibit a large intrinsic anomalous Hall effect originating from the Berry curvature. To employ this large Hall current for room temperature topo-spintronics applications, it is necessary to fabricate these materials as thin or ultrathin films. Here, we experimentally demonstrate that Weyl semimetal Co 2 MnGa thin films (20–50 nm) show a large anomalous Hall angle ~11.4% at low temperature and ~9.7% at room temperature, which can be ascribed to the non-trivial topology of the band structure with large intrinsic Berry curvature. However, the anomalous Hall angle decreases significantly with thicknesses below 20 nm, which band structure calculations confirm is due to the reduction of the majority spin contribution to the Berry curvature. Our results suggest that Co 2 MnGa is an excellent material to realize room temperature topo-spintronics applications; however, the significant thickness dependence of the Berry curvature has important implications for thin-film device design.