Effect of Cr2O3 on the crystallization, structure, and properties of Ti-bearing blast furnace slag-based glass ceramics
JOURNAL OF ASIAN CERAMIC SOCIETIES(2021)
摘要
The effects of Cr2O3 on the crystallization, structure, and properties of Ti-bearing blast furnace slag-based glass ceramics were investigated. The results show that the transition temperature and crystallization temperature decreased with introduction of Cr2O3 as a while. Specifically, the crystallization temperature first decreased, then increased with the increase Cr2O3 concentration from 0.2 wt% to 0.8 wt%, and finally decreased with further increased in Cr2O3 concentration. The crystal phases were identified as anorthite, diopside, and akermanite. As the content of Cr2O3 increased to 0.8 wt%, the dendrites gradually decreased and the granular crystals gradually increased. When the Cr2O3 concentration further increased, the number of granular crystals gradually decreased and the dendrites gradually accumulated. With the increase of Cr2O3 from 0.2 wt% to 0.8 wt%, the structure of the investigated glass gradually depolymerized, while the opposite trend was presented with further increased in Cr2O3 content. With increasing Cr2O3 content from 0.2 wt% to 2 wt%, the flexural strength values and Vickers hardness values of the glass ceramics first increased and then decreased, and the maximum values of flexural strength and Vickers hardness were obtained as 94.371MPa and 974.43MPa, respectively. The prepared Ti-bearing blast furnace slag-based glass ceramics showed good acid and alkali resistance.
更多查看译文
关键词
Ti-bearing blast furnace slag,Cr2O3,glass ceramics,crystallization
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要