Corrosion Cracking Process of Reinforced Concrete under the Coupled Effects of Chloride and Fatigue Loading
KSCE JOURNAL OF CIVIL ENGINEERING(2021)
摘要
To study the corrosion cracking process of reinforced concrete under the combined effects of chloride and fatigue loading, the constan-current and dry-wet cycle accelerated corrosion method was used to corrosion the specimens under different stress levels for different time. The quality loss of reinforcement, the composition of corrosion products and the cracking of concrete are analyzed from the macro, micro and micro scales, and to obtain the spatial distribution as well as microscopic characteristics of corrosion products of the reinforcement bar under coupling conditions. Additionally, a model of steel rust cracking under the coupled action of chloride and fatigue loading is established. The results show that: under the same corrosion time, the concrete cracking and steel corrosion degree become more serious with the increase of stress level. The greater the stress level, the earlier corrosion occurs and the more corrosion products are, Moreover, due to the fatigue load, the concrete on the upper side of the steel bar has rust expansion cracks earlier than the lower side.
更多查看译文
关键词
Coupled effect,Corrosion products,Model of steel rust cracking,Corrosion cracking process,Microscopic characteristics
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要