Phosphotungstic Acid Intercalated Zn,Al-Layered Double Hydroxides/ Nanocellulose Based 3d Lightweight Foam Thermal Insulation Materials
MATERIALS RESEARCH EXPRESS(2021)
摘要
In this study, [PW12O40](3-) anions have been intercalated into Zn,Al-Layered Double Hydroxides(ZnAl-NO3-LDHs) to synthesize ZnAl-PW12O40-LDHs by ion-exchange reaction. The chemical composition and structure were analyzed by XRD, FT-IR, ICP, and SEM. Then, the nanocellulose based 3D lightweight foam thermal insulation materials was prepared by ZnAl-PW12O40-LDHs and CNF compound with H3BO3. The TG showed that ZnAl-PW12O40- LDHs significantly reduced the maximum decomposition rate and increased the carbon residual rate at 800 degrees C, which indicated that ZnAl-PW12O40-LDHs can improve the oxidation resistance of CNF composite materials at high temperature.The fire resistance of different samples were evaluated by back temperature test and alcohol lamp flame test, CNF/50%ZnAl-PW12O40-LDHs /2%H3BO3 showed best thermal stability and flame-retardant properties, which can be contributed to the decomposition products of ZnAl-PW12O40-LDHs, acting both as phase flame retardant and condensed phase flame retardant.
更多查看译文
关键词
layered double hydroxides, phosphotungstic acid, thermal insulation, flame, retardant properties, nanocellulose
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要