Sealing Treatment of Plasma-Sprayed Cr3C2-NiCr/Al2O3-TiO2 sub> Coating by Aluminum Phosphate Sealant Containing Al2O3 Nanoparticles
JOURNAL OF THERMAL SPRAY TECHNOLOGY(2022)
Abstract
A typical structure of thermal spray coatings consisted of molten particles, semi-molten particles, oxides, pores, and cracks. These factors caused the porosity of sprayed coatings, leading to a significant influence on the coating properties, especially their wear-corrosion resistance. In this study, a post-spray sealing treatment of Cr3C2-NiCr/Al2O3-TiO2 plasma-sprayed coatings was carried out, and then, their corrosion properties were evaluated, before and after the treatment. For the sealing process, aluminum phosphate (APP) containing Al2O3 nanoparticles (similar to 10 nm) was used. The permeability of APP into the sprayed coating was analyzed by SEM-EDS. The treatment efficiency for porosity and corrosion resistance of sprayed coatings was evaluated by electrochemical measurements, such as the potentiodynamic polarization and electrochemical impedance spectroscopy. The wear-corrosion resistance of the coating was examined in 3.5 wt.% NaCl circulation solution containing 0.25% SiO2 particles. The sealing efficiency was evaluated by the percentage of the treated open pores in the coating. The obtained results showed that APP penetrated deeply through the coating and the incorporation of Al2O3 nanoparticles into APP sealant improved the sealing efficiency by 20% of open pores in comparison with the sealant without nano-Al2O3. The effect of the post-treatment on corrosion protection of the sprayed coating has been discussed.
MoreTranslated text
Key words
aluminum phosphate sealant,corrosion,Cr3C2-NiCr,Al2O3-TiO2,impregnation,nano-Al2O3,plasma spraying
AI Read Science
Must-Reading Tree
Example
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
Generate MRT to find the research sequence of this paper
Chat Paper
Summary is being generated by the instructions you defined