17-4 PH stainless steel has proven to be one of the workhorse materials in industries such as aerospace, chemical, and energy. The attraction of this alloy to the aforementioned industries is derived from the fact that 17-4 PH stainless steel possesses a combination of excellent mechanical properties and corrosion resistance. Manufacturing of 17-4 PH stainless steel through 3D printing will further inspire confidence in the aforementioned industries. The current study investigated the effects of LENS process parameters on porosity, microstructure, and microhardnesss. The scanning speed and powder feed rate were varied at 7.62 mm/s-12.7 mm/s and 4.70 g/min-5.98 g/min rpm, respectively, while laser power was kept constant at 300 W. The optimum scanning for both 4.70 g/min and 5.98 g/min was 10. 16 mm/s and 12.7 mm/s, respectively. The current study deduced that varying both scanning speed and powder feed rate had an impact on both the microstructure and microhardness.
更多查看译文
关键词
17-4 PH stainless steel, LENS, Microhardness, Microstructure, Porosity
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要