Na3+Xmxp1-Xs4 (M = Ge4+, Ti4+, Sn4+) Enables High Rate All-Solid-State Na-Ion Batteries Na2+2 Delta Fe2-Delta(So4)(3)Vertical Bar Na3+Xmxp1-Xs4 Vertical Bar Na2ti3o7

Electrolytes in current Na-ion batteries are mostly based on the same fundamental chemistry as those in Li-ion batteries a mixture of flammable liquid cyclic and linear organic carbonates leading to the same safety concerns especially during fast charging. All-solid-state Na-ion rechargeable batteries utilizing non-flammable ceramic Na superionic conductor electrolytes are a promising alternative. Among the known sodium conducting electrolytes the cubic Na3PS4 phase has relatively high sodium ion conductivity exceeding 10(-4) S cm(-1) at room temperature. Here we systematically study the doping of Na3PS4 with Ge4+ , Ti4+ , Sn4+ and optimise the processing of these phases. A maximum ionic conductivity of 2.5 X 10(-4) S cm(-1) is achieved for Na3.1Sn0.1P0.9S4. Utilising this fast Na+ ion conductor, a new class of all-solid-state Na2+2 delta Fe2-delta(SO4)(3)|Na3+xMxP1-xS4 (M = Ge4+, Ti4+, Sn4+) (x = 0,0.1)|Na2Ti3O7 sodium-ion secondary batteries is demonstrated that is based on earth-abundant safe materials and features high rate capability even at room temperature. All-solid-state Na2+2 delta Fe2-delta(SO4)(3)|Na3+xMxP1-xS4|Na2Ti3O7 cells with the newly prepared electrolyte exhibited chargedischarge cycles at room temperature between 1.5 V and 4.0 V. At low rates the initial capacity matches the theoretical capacity of ca. 113 mA h g(-1). At 2C rate the first discharge capacity at room temperature is still 83 mA h per gram of Na2+2 delta Fe2-delta(SO4)(3) and at 80 degrees C it rises to 109 mA h per gram with 80% capacity retention over 100 cycles.