Conversion Of Polymer Surfaces Into Nonwetting Substrates For Liquid Metal Applications

Liquid metal-based applications are limited by the wetting nature of polymers toward surface-oxidized gallium-based liquid metals. This work demonstrates that a 120 s CF4/O-2 plasma treatment of polymer surfaces-such as poly(dimethylsiloxane) (PDMS), SU8, S1813, and polyimide-converts these previously wetting surfaces to nonwetting surfaces for gallium-based liquid metals. Static and advancing contact angles of all plasma-treated surfaces are >150 degrees, and receding contact angles are >140 degrees, with contact angle hysteresis in the range of 8.2-10.7 degrees, collectively indicating lyophobic behavior. This lyophobic behavior is attributed to the plasma simultaneously fluorinating the surface while creating sub-micron scale roughness. X-ray photoelectron spectroscopy (XPS) results show a large presence of fluorine at the surface, indicating fluorination of surface methyl groups, while atomic force microscopy (AFM) results show that plasma-treated surfaces have an order of magnitude greater surface roughness than pristine surfaces, indicating a Cassie-Baxter state, which suggests that surface roughness is the primary cause of the nonwetting property, with surface chemistry making a smaller contribution. Solid surface free energy values for all plasma-treated surfaces were found to be generally lower than the pristine surfaces, indicating that this process can be used to make similar classes of polymers nonwetting to gallium-based liquid metals.