Chromatic Conductive Polymer Nanocomposites Of Poly (P-Phenylene Ethynylene)S And Single-Walled Carbon Nanotubes

We report on dispersions and thin films of chromatic conductive nanocomposites of poly(p-phenylene ethynylene)s (PPEs) and single-walled carbon nanotubes (SWNTs) generated via solution mixing. The linear, conjugated PPEs with dialkyl- and dialkyloxy-side chain groups are shown to debundle and disperse high concentration (up to 2.5 mg/mL) SWNTs in various organic solvents. The solubilization of SWNTs and PPE wrapping is accompanied with the change in the solution color. Ultraviolet visible absorption spectra of nanocomposite solutions demonstrate a new absorption peak at a higher wavelength, supporting the observed chromatism. Fluorescence spectra of nanocomposite solutions display significant quenching of the fluorescence intensity and the Stern-Volmer model is used to analyze fluorescence quenching. Electron microscopy of the chromatic solid films of high mass fraction PPE/SWNT nanocomposites obtained by vacuum filtration reveals the debundled SWNTs in the PPE matrix. The tensile strength and Young's modulus of these PPE/SWNT nanocomposite films are as high as 150 MPa and 15 GPa, respectively. The composite films exhibit remarkably high conductivities, ranging from similar to 1000 S/m to similar to 10,000 S/m for 10 wt% and 60 wt% SWNT nanocomposites, respectively.