Orientation Control Of Carbon Fibers And Enhanced Thermal/Mechanical Properties Of Hot-Extruded Carbon Fibers/Aluminum Composites

DIAMOND AND RELATED MATERIALS(2021)

引用 15|浏览2
暂无评分
摘要
Electroless nickel (Ni)-coated carbon fibers (CFs)/aluminum (Al) composites were prepared by a hot-extrusion process. The effects of Ni-coating and extrusion temperature on microstructure, thermal conductivity (TC), coefficient of thermal expansion (CTE), and compressive strength of CFs/Al composites have been systematically investigated. Microstructural observations showed that the CFs in hot-extruded composites were preferentially oriented along the extrusion direction. The Ni coating on CFs resulted in higher relative density of CFs/Al composites, more homogeneous distributions of CFs in the Al matrix, and stronger interfacial bonding between CFs and Al. As a result, the extruded Ni-coated CFs/Al samples showed higher TC, lower CTE, and higher compressive strength in comparison with uncoated CFs/Al extruded samples and Ni-coated CFs/Al spark plasma sintered (SPSed) samples. For example, the Ni-coated CFs/Al sample extruded at 500 degrees C showed TC, CTE, and compressive strength values of 227 W m(-1) K-1, 7.32 ppm K-1, and 113 MPa, respectively, which correspond to 18%, -22%, and 38% enhancements compared to the SPSed sample.
更多
查看译文
关键词
Electroless nickel coating, Hot extrusion, Carbon fibers/Al composite, Thermal conductivity, Coefficient of thermal expansion, Compressive strength
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要