Observation of table-like magnetocaloric effect and large refrigerant capacity in Nd6Fe13Pd1–xCux compounds

The table-like magnetocaloric effect is significant for the magnetic refrigeration applications above 20 K based on the Ericsson cycle. Herein, we prepared a series of Nd6Fe13Pd1–xCux (x = 0.05, 0.1, 0.15) compounds by the arc-melting method. These compounds show the single crystalline phase in the tetragonal Nd6Fe13Si-type structure with the space group I4/mcm. A magnetic phase transition from ferromagnetism to antiferromagnetism and a metamagnetic transition from the antiferromagnetic state to the ferromagnetic state are observed in each of the compounds. The compounds exhibit table-like magnetocaloric effects with large refrigerant capacities. A constant ΔSM in a temperature span of 40 K in the Nd6Fe13Pd0.85Cu0.15 compound are observed. For a field change of 0–5 T, the peak values of –ΔSM for the Nd6Fe13Pd0.95Cu0.05, Nd6Fe13Pd0.90Cu0.10, and Nd6Fe13Pd0.85Cu0.15 compounds are estimated to be 4.8, 4.6 and 4.4 J/(kg·K) with corresponding refrigerant capacity values of 323, 331 and 316 J/kg, respectively. The obtained table-like magnetocaloric effects with large refrigerant capacities as well as fairly small thermal and magnetic hysteresis deem these series of compounds good candidates for single-phase magnetic refrigeration based on the Ericsson cycle.