Influence Of Calcination Temperature On Microstructure And Properties Of (Nicuzn)Fe2o4 Ferrite Prepared Via Ultrasonic-Assisted Co-Precipitation
JOURNAL OF SUPERCONDUCTIVITY AND NOVEL MAGNETISM(2021)
Abstract
(NiCuZn)Fe2O4 ferrite is a kind of soft magnetic material widely used in multilayer chip inductors because of its high resistivity and excellent magnetic properties at high frequencies. In this study, (Ni0.4Cu0.2Zn0.4)Fe2O4 ferrite powder was prepared by ultrasonic-assisted chemical co-precipitation method, the effect of calcination temperature on the structure and properties of ferrite powders was investigated by modern analytical methods that include differential thermal analysis, X-ray diffraction, transmission electron microscopy, infrared spectroscopy, and vibrating sample magnetometer, respectively. The results show that the grain size increased from 23.5 nm to 38.6 nm and the lattice size increased from 8.384 angstrom to 8.390 angstrom with the increase of calcination temperature from 600 degrees C to 900 degrees C. The TEM shows that the powder particle was uniform and dispersible, and the particle size was about 30nm at 800 degrees C calcination. The saturation magnetization of ferrite powder increases from 45.85emu/g to 50.65emu/g and the coercivity decreases from 65.50Oe to 46.23Oe with the increase of calcination temperature from 700 degrees C to 900 degrees C. The uniform and fine nano-crystalline ferrite particles would reduce the sintering temperature and improve the stability of the properties for spinel ferrite. The preparation of nano-spinel ferrite by ultrasonic-assisted co-precipitation is a worthy wet process for application.
MoreTranslated text
Key words
Soft magnetic ferrite, Co-precipitation synthesis, Ultrasonic assisted, Magnetic properties
AI Read Science
Must-Reading Tree
Example
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
Generate MRT to find the research sequence of this paper
Chat Paper
Summary is being generated by the instructions you defined