Structural And Magnetic Characterizations Of Nixcu0.8-X Zn0.2fe2o4 Spinel Ferrites

The Ni-Cu-Zn ferrites are one of the most exciting spinel oxides so far because of its diverse applications. In the current study, the ratio of nickel and copper was varied keeping the concentration of zinc constant primarily aiming to examine its effect on cation distribution as well as structural and magnetic properties. The samples were synthesized via the conventional solid state sintering method at a temperature of 1050 degrees C then subjected to neutron diffraction studies. The magnetic properties were measured using a vibrating sample magnetometer (VSM) which complements the magnetic measurements from the neutron diffraction experiments. The ferromagnetic behaviors of these Ni-Cu-Zn ferrites were explained using the Y-K model and the canting of the magnetic moments were also measured. The lattice parameter 'a' was seen to reduce which results from the replacement of large Cuthorn ions (0.73A degrees) with the smaller ionic radius of Ni+(0.69 A degrees). To accommodate a large number of cations in the spinel lattice, the oxygen atoms restructure themselves as a result oxygen position parameter increased. The net magnetic moment per unit formula decreases as the Ni content is increased up to a level, after which the net moment increased.