Microstructure And Oxidation Behaviour Of Mosi2 Coating Combined Mob Diffusion Barrier Layer On Mo Substrate At 1300 Degrees C
Ceramics International(2021)
Abstract
To improve the oxidation resistance of a Mo substrate at high temperatures, MoSi2-MoB double layers were prepared on the surface of the substrate using a two-step pack cementation method. The isothermal oxidation tests indicate that the weight loss of MoSi2-MoB double layers was only 6.3824 mg/cm(2) after oxidation at 1300 degrees C for 15 h, whereas the untreated Mo experienced serious weight loss and the weight loss was 606.775 mg/cm(2) after only 90 min. Following oxidation exposure, the oxidized coating became six complex layers due to correlation diffusion among Mo, Si and B. The double layers showed excellent high-temperature oxidation resistance due to the formation of a dense and continuous SiO2 layer with low O-2 permeability. Meanwhile, in situ fabrication of a novel Mo5SiB2 layer could prevent inward diffusion of Si.
MoreTranslated text
Key words
Silicide coating, Two-step pack cementation, Diffusion barrier, Oxidation, Molybdenum
AI Read Science
Must-Reading Tree
Example
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
Generate MRT to find the research sequence of this paper
Chat Paper
Summary is being generated by the instructions you defined