Effects of 2% sodium fluoride solution on the prevention of streptococcal adhesion to titanium and zirconia surfaces

Streptococci are associated with dental plaque formation as the early-colonizing bacteria that adhere to titanium (CpTi) and zirconia (TZP) implant abutment surfaces. Effective prevention of peri-implantitis may be possible by removing streptococci as target. This study aimed to evaluate the effects of 2% NaF on the prevention of streptococcal adhesion to CpTi and TZP. After immersion in 2% NaF for 90 min, surface characterization of mirror-polished CpTi and TZP disks were assesed using XPS, EPMA, and SEM. S. sanguinis , S. gordonii , and S. oralis were used as the streptococcal bacterial strains. After 24 h culture, bacterial adhesion was evaluated using an ATP-bioluminescent assay and SEM. In XPS, EPMA, and SEM analyses, fluoride was detected on the CpTi and TZP surfaces after 2% NaF immersion with no signs of localization, and no corrosion on the CpTi disks. Based on the adhesion assay, the adherences of S. sanguinis , S. gordonii , and S. oralis were significantly lower with NaF than without NaF in CpTi ( p = 0.005, 0.001, and 0.001, respectively) and TZP ( p = 0.003, 0.002, and 0.001). This was also confirmed by SEM. In conclusion, 2% NaF reduced the adhesion of streptococci to the CpTi and TZP surfaces.