Investigation On Mechanical Properties Of Gh4720li At High Strain Rates At Wider Temperature Range

In this paper, the dynamic mechanical properties of GH4720Li nickel-base alloy under a large temperature range and high and low strain rates were studied by the hot compression test. The difference of mechanical properties of GH4720Li alloy under high and low strain rates was analyzed from the perspective of microstructure. The hot compression test experimental results showed that the true stress of GH4720Li alloy decreased at a low strain rate as the trial temperature elevated. Nevertheless, it was abnormal that the true stress increased at high strain rate condition as temperature elevated. By comparing the microstructure under high and low strain rates, it was found that the precipitates under low strain conditions contained a large amount of Cr (Mo). However, the content of Cr (Mo) in the precipitates at a high strain rate decreased, while the content of Fe increased. It would be concluded that Cr (Mo) would reduce the compressive strength and plasticity of GH4720Li alloy, while Fe would increase the compressive strength and plasticity of GH4720Li alloy. In addition, under the condition of a low strain rate, the shape of Cr (Mo) precipitates obtained at 20 degrees C was lamellar, but it was spherical at 800 degrees C. The compressive strength of GH4720Li composites with lamellar precipitates was higher than that of spherical precipitates.