UV response characteristics of mixed-phase MgZnO thin films with different structure distributions, high Iuv/Idark ratios, and fast speed MgZnO UV detectors with tunneling breakdown mechanisms.

High-performance ultraviolet (UV) detectors with both high responses and fast speeds are hard to make on homogeneous crystal semiconductor materials. Here, the UV response characteristics of mixed-phase MgZnO thin films with different internal structure distributions are studied. The mixed-phase MgZnO-based detector with the given crystal composition has a high response at both deep UV light (96 A W-1 at 240 nm) and near UV light (80 A W-1 at 335 nm). Meanwhile, because of the quasi-tunneling breakdown mechanism within the device, the high-response UV detector also shows a fast response speed (tr = 0.11 μs) and recovery speed (td1 = 26 μs) at deep UV light, which is much faster than both low-response mixed-phase MgZnO-based UV detectors with other structure constitutions and reported high-response UV devices on homogenous crystal materials. The Idark of the device is just 4.27 pA under a 5 V bias voltage, so the signal-to-noise ratio of the device reached 23852 at 5.5 uW cm-2 235 nm UV light. The new quasi-tunneling breakdown mechanism is observed in some mixed-phase MgZnO thin films that contain both c-MgZnO and h-MgZnO parts, which introduce a high response, signal-to-noise ratio, and fast speed into mixed-phase MgZnO-based UV detectors at weak deep UV light.