Pd Supported On Mil-68(In)-Derived In2o3 Nanotubes As Superior Catalysts To Boost Co2 Hydrogenation To Methanol

Utilization of CO2 and its conversion to value-added chemicals are highly desirable to alleviate the environmental concerns caused by the massive anthropogenic CO2 emission. Although In2O3/Pd have been employed as efficient catalysts for hydrogenation of CO2 to methanol, the electronic effects by strong metal-support interaction (SMSI) between Pd and In2O3 are poorly understood, which is greatly affected by the morphology of In2O3. Herein, we use MIL-68(In) nanorod as a morphological template for the synthesis of hollow In2O3 nanotubes (h-In2O3) and the preparation of supported Pd catalysts for CO2 hydrogenation to methanol. Interestingly, loading Pd on h-In2O3 showed a much higher performance than In2O3 with other morphologies, which exhibited almost unchanged CO2 conversion of 10.5%, methanol selectively of 72.4%, and methanol space-time yield of 0.53 g(MeOH) h(-1) g(cat)(-1) over 100 h on stream at 3 MPa and 295 degrees C. After in-depth characterizations, we found that the different electronic properties of Pd species on In2O3 can be finely tuned by diverse synthetic conditions, which were responsible for high activity and stability. The molar fraction of Pd2+ species in the h-In2O3/Pd catalyst reached 67.6%, 3.2 times that of the In2O3@Pd catalyst (21.3%), due to the different surface chemistry of In2O3. Density function theory results indicated that the Pd donated more electrons to the curved In2O3 (222) surface than the pristine surface, and Pd2+ was critical to facilitate H-2 adsorption and formation of the surface oxygen vacancy. This work demonstrates that controlling the morphology of In2O3 can modify both the Pd electronic property and SMSI between Pd and In2O3, which are the origins of the high catalytic performance.