Microstructures, mechanical properties, and grease-lubricated sliding wear behavior of Cu-15Ni-8Sn-0.8Nb alloy with high strength and toughness
Friction(2021)
摘要
Alloys used as bearings in aircraft landing gear are required to reduce friction and wear as well as improve the load-carrying capability due to the increased aircraft weights. Cu-15Ni-8Sn-0.8Nb alloy is well known for possessing good mechanical and wear properties that satisfy such requirements. In this study, the microstructure, mechanical properties, and grease-lubricated sliding wear behavior of Cu-15Ni-8Sn-0.8Nb alloy with 0.8 wt% Nb are investigated. The nanoscale NbNi3 and NbNi2Sn compounds can strengthen the alloy through the Orowan strengthening mechanism. A Stribeck-like curve is plotted to illustrate the relationship among friction coefficient, normal load, and sliding velocity and to analyze the grease-lubricated mechanism. The wear rate increases with normal load and decreases with sliding velocity, except at 2.58 m/s. A wear mechanism map has been developed to exhibit the dominant wear mechanisms under various friction conditions. When the normal load is 700 N and the sliding velocity is 2.58 m/s, a chemical reaction between the lubricating grease and friction pairs occurs, resulting in the failure of lubricating grease and an increase in wear.
更多查看译文
关键词
Cu-15Ni-8Sn-0.8Nb alloy,microstructure,mechanical properties,grease-lubricated wear behavior
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要