Mechanical, Morphological, Flamability And Thermal Properties Of Artificial Wood Plastic

Purpose The purpose of this study is to manufacture composites from sawdust and polymer high-density polyethylene (HDPE) with different loading from alum as natural and cheap flame retardant and subsequently characterized using standard analytical tools. Design/methodology/approach Artificial wood plastic composites (WPCs) were prepared by mixing HDPE with sawdust as a filler with constant ratio (2:1) using hot press. Polyethylene-graft-maleic anhydride (PE-g-MAH) used as a coupling agent between two parents of the composites with different ratios (2.5, 5, 7 and 10). Alum as a flame retardant was incorporated into HDPE with 5 phr polyethylene grafted with maleic anhydride (PE-g-MAH) with different ratios (10, 15 and 20). Flame retardant efficiency was investigated using differential scanning calorimetry, thermal gravimetric analysis and the technique of ASTM E162. Findings The results revealed that the composite containing 5 phr from (PE-g-MAH) exhibited higher mechanical properties and this proved that (PE-g-MAH) act as an efficient coupling agent using the aforementioned ratio. The results also revealed that incorporation of alum as a flame retardant increased the thermal stability of the composites. Originality/value Artificial WPCs are ecofriendly materials with a wide range of applications in the constructions field. Moreover, they have high mechanical and physical properties with low cost. Evaluate alum as a natural and cheap flame retardant.