Strengthening Effect Of Laser Shock Peening On 7075-T6 Aviation Aluminum Alloy

The strengthening effect and uniformity of residual stress and strain of 7075-T6 aviation aluminum after laser shock peening were investigated. The finite element simulation model of laser shot peening on 7075-T6 aviation aluminum alloy was established and verified. On this basis and combined with experiment, the microstructure, residual stress distribution and equivalent strain distribution of 7075-T6 aviation aluminum alloy after laser shock peening were studied. An indexUfor evaluating the strain uniformity in the peened area was proposed based on the statistical processing of the equivalent strain distribution in the peened area. The results show that the average grain size on the peened surface of the specimen was refined to 20-30 mu m after LSP, and a residual compressive stress layer with thickness of about 0.5 mm was induced on the surface. Grain refinement and residual compressive stress can promote the strength and fatigue properties of 7075-T6 aviation aluminum alloy. The minimum value ofUis obtained in the 6 x 6 spot array (the corresponding overlap ratio is 58%), which suggest that the most uniform deformation peened area can be obtained by using 58% overlap ratio in the laser shot peening process, which can avoid stress concentration and improve fatigue life.