Gold-Silver Electroless Plating On Laser Powder-Bed Fusion Additively Printed Alsi10mg Parts

METALS(2020)

引用 8|浏览8
暂无评分
摘要
The current research presents a novel methodology for surface finishing of printed AlSi10Mg parts by electroless deposited gold-silver (electrum) alloys. The parts were printed by additive manufacturing laser powder-bed fusion (AM-LPBF). The electrum was chosen due to its appearance and good electrical and thermal properties and was deposited on disk-shaped specimens at 80 and 90 degrees C. The coating quality and appearance were studied by different methods for various deposition times and film thicknesses. The results indicate that Au-Ag coatings of AM-LPBF AlSi10Mg yield satisfactory results. The XRD analysis revealed that the coatings were composed of Au-Ag crystalline phases and beneath them, a quasi-amorphous or mixed quasi-amorphous and nanocrystalline Ni-P interlayer. The mechanism of electrum formation was studied based on the XPS analysis results as a function of the temperature and concentration. At 80 degrees C, the Ag was dominant at the beginning of the deposition process, while at 90 degrees C the Au was first detected on the interface. This result was explained by the electrochemical properties of alloying metals and the binding energies required to form metal-Ni and Au-Ag bonding. The results indicate that the electrum coatings are satisfactory, and the developed surface finishing process could be used for many applications.
更多
查看译文
关键词
additive manufacturing,AlSi10Mg substrate,electroless plating,gold-silver coating,NiP interlayer,laser powder-bed fusion
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要