Microstructure and mechanical properties of Cu-ZTA cermet prepared by vacuum hot pressing sintering
MATERIALS RESEARCH EXPRESS(2020)
摘要
In this paper, seven copper-zirconia toughened alumina (Cu-ZTA) cermets were prepared by vacuum hot pressing sintering (VHP). The effects of different binder content and different particle size of ZTA particles on the mechanical properties of Cu-ZTA cermets were investigated. The microstructure of the composites was studied by x-ray diffraction, scanning electron microscopy and energy dispersive spectroscopy. The hardness of the material was measured by micro Vickers hardness tester. The results show that the solid solution strengthening occurs in the hot pressing sintering process, the formation of copper-based solid solution increases the hardness of the matrix, the highest is 192.04 HV0.1. The ZTA particles are uniformly distributed in the matrix, and the surface of the ZTA particles is surrounded by a continuous coppermatrix and second phase. Two interfaces are formed between ZTA particles and Cu matrix. One is the ZTA/Cu interface formed by the substitution of Cu atoms for Ni atoms, it is a mechanical meshing interface which extends the service life of cermet under mechanical stress and thermal stress. The other interface is the reaction bonding interface of Cu3Ti3O and TiOx. The friction and wear test results show that the use of low-diameter ZTA particles and increasing the content of Cu binder will improve the friction and wear properties of Cu-ZTA cermet. Under the action of stress, the fracture occurs at the interface of Cu/ZTA, and the wear, fracture and extraction of ZTA ceramics cause the failure of Cu-ZTA cermet.
更多查看译文
关键词
powder metallurgy,vacuum hot pressing sintering,cermet,interface bonding
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要