Magnetic Properties of Mn1.9Cu0.1Sb under High Pressure

Magnetization measurements were carried out for polycrystalline Mn1.9Cu0.1Sb in magnetic fields up to 5 T in the 10-300 K temperature range under high pressures up to 1 GPa in order to investigate the magnetic properties and the thermal transformation arrest (TTA) phenomenon under high pressures. The spin-reorientation temperature increased from 202 K for 0.1 MPa to 244 K for 1 GPa, whereas the transition temperature from the ferrimagnetic (FRI) to antiferromagnetic (AFM) state did not drastically change at similar to 116 K. The magnetic relaxation behavior from the FRI to AFM state was observed in 10 < T <= 70 K, which was analyzed using the Kohlrausch-Williams-Watts model. Obtained results indicated that the TTA phenomenon of Mn1.9Cu0.1Sb was suppressed by the application of high pressures.