Water Resistance and Thermal Properties of Polyvinyl Alcohol-Starch Fiber Blend Film
AIP Conference Proceedings(2017)
摘要
The growing attention of starch fiber (SF) has led to the innovation of Polyvinyl Alcohol-SF (PVA-SF) blends. This blend is regarded as the biodegradable material which aims to reduce the accumulation of synthetic polymer solid waste derived from petroleum. In this study, the thermal blending characterizations of 1.)VA-SF were investigated by differential scanning calorimetry (DSC), and thenuogravimetric analysis (TGA). The water resistance of the blend was also evaluated to study the polarity of the blends. The blend was prepared by plasticizing the polyvinyl alcohol with glycerol and distilled water with the addition of starch fiber. The incorporation of SF to the blends was at 10 wt% to 50 wt% composition. Based on the thermal analysis, PVA-SF blends were suitable for processing at high temperatures, which can be seen by the shifted onset degradation temperature to a higher temperature. This is because cyclic hemiacetals which were provided by SF can act to prevent the thermal attacks. Conversely, increasing the starch fiber proportion to the film blend reduce the endothermic peak amplitude in the DSC thermogram. It was found that PVA-SF blend at the higher composition of SF had the highest water resistance. This may be attributed to the content of fibre in SF which is hydrophilic.
更多查看译文
关键词
Starch fiber (SF),Polyvinyl alcohol (PVA),Thermal properties,Biopolymers
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要