Molecular Beam Epitaxy (MBE) was used to grow GaSb thin films on GaSb substrates. We have obtained the optimized growth condition to improve films quality and the surface morphology of GaSb epilayer during growth. Two group samples were tested to study the influence of the growth rate and the V/III flux ratios on the crystal quality. It caused fewer defects when the growth rate of approximately was fixed 0.6 ML/s. And the surface morphology and performance was best for GaSb epilayer when the beam ratio was 5. The thin films were characterized by Atomic Force Microscopy (AFM) and high-resolution X-Ray Diffraction (XRD). The root means square roughness of the superlattice surface was only 0.335 nm. The full width at half maximum of the rocking curve was 39.6 arcsec and the emission wavelength of photoluminescence was 1.99 mu m.
更多查看译文
关键词
Homoepitaxial, molecular beam epitaxy, GaSb films, growth rate, V, III flux
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要