Highly Porous Ni-P Electrode Synthesized by an Ultrafast Electrodeposition Process for Efficient Overall Water Electrolysis

The development of high-efficiency catalysts for hydrogen evolution reaction (HER) and oxygen evolution reaction (OER) is essential to lower the energy losses during water electrolysis. Herein, a highly porous Ni-P (HP Ni-P) electrode, prepared by an ultrafast electrodeposition within only ten seconds, is presented with superior electrocatalytic activity towards both HER and OER in alkaline media: overpotentials of 96 and 323 mV are required to reach a current density level of 100 mA cm(-2)for HER and OER, respectively, with corresponding Tafel slopes of 32.9 and 44.0 mV dec(-1). Experimental analyses and theoretical calculations show that charge transfer occurs from Ni to P and the HER kinetics is accelerated by the increased hydrogen coverage, enhanced water dissociation ability, and optimized hydrogen adsorption energy on the HP Ni-P. Under OER conditions, surface P is oxidized into PO43-, promoting oxidation of Ni to OER-active NiOOH and exposing abundant OER-active sites on the HP Ni-P surface. An alkaline electrolysis cell was constructed with HP Ni-P as the cathode and anode (Ni-P||Ni-P) and outperformed the Pt/C||IrO(2)cell at cell voltages exceeding 1.68 V. This work provides a practically applicable method to prepare HER and OER electrodes for use in industrial water electrolyzers, with insight into the activities of the catalysts.