The effect of fibre length and matrix modification on the fire performance of thermoplastic composites: The behaviour of PP as an example of non-charring matrix

The fire performance of fibre-reinforced polypropylene (PP) was investigated with respect to fibre length and modification of the matrix. Fibre lengths of 3 mm, 12 mm, and continuous fibres were used as reinforcements. E-glass continuous fabrics were melt impregnated with PP and consolidated via compression moulding. E-glass fibre-reinforced PP pellets of 3 and 12 mm were compression moulded. Cone calorimetry tests with incident radiant fluxes of 20, 30 and 35 kW m(-2) were used to investigate the fire properties of PP glass fibre composites. Results showed that continuous glass fibre reinforced PP exhibits the best fire performance at 20 kW m(-2), while 3-mm fibre has the best performance at 35 kW m(-2); 12-mm fibre-reinforced PP exhibitedthe lowest performance in comparison with 3-mm and continuous glass fibre reinforcement. Melic-anhydride (MA)-modified PP was found to increase the heat release rate (HRR) by up to 44% and time to ignition by up to 10% depending on the heat flux applied in comparison with unmodified PP. The glass fibre-reinforced composite made with MA-modified PP has 5-12% lower mean HRR and similar time to ignition in comparison with glass fibre composite made by unmodified PP. This suggests improved fibre adhesion plays a role of the fire performance of glass fibre-reinforced PP.