COMPETITIVE LIFE TIME ASSESSMENT OF SrO-ZTA/SrO-ZTA AND CoCrMo/UHMWPE HIP PROSTHESIS BEARINGS

The hip joint envisages the prime load bearing structure among other joints in the human body. Hip joint failure leads to the replacement of the hip joint prosthesis. This research work focuses on the proper selection of bearing couple materials for the hip joint to improve the performance and life. Herein, the stress and deformation of different bearing couple materials are analysed in the perspective of transient dynamic analysis under jogging load cycle. Selective hip joint bearing (femoral head-liner) couples are SS316L on UHMWPE (MoP), CoCrMo on UHMWPE (MoP), Ti6Al4V on SrO-ZTA (MoC), SrO-ZTA on UHMWPE (CoP) and SrO-ZTA on SrO-ZTA (CoC) encountered, respectively. The SrO-ZTA on SrO-ZTA (CoC) bearing couple generates the less Von Mises stress of 180.88 MPa. Load bearing pressure and Archard law predict the wear depth of CoCrMo on UHMWPE (MoP) and SrO-ZTA on SrO-ZTA (CoC) bearing couples are 0.141 mm/year and 0.031 mm/year, respectively. In simultaneous, the theoretical wear volume for CoCrMo on UHMWPE (MoP) and SrO-ZTA on SrO-ZTA (CoC) bearing couples are found as 35.46 mm(3)/year and 2.62 mm(3)/year, respectively. The wear depth and wear volume are supporting the available clinical retrievals and exist in well acceptable range. Competitive wear analysis data ensures 15 years safe life of SrO-ZTA on SrO-ZTA (CoC) hip prosthesis bearing.