The Influence On Healing Of Bony Window Elevated Inward In The Sinus Cavity As Cortical Bone Graft: A Histomorphometric Study In Rabbit Model

Purpose: To evaluate the influence on healing of the bony window elevated inward in the sinus cavity as a cortical bone graft. Materials and Methods: Eighteen rabbits were included in the experiment. At the test sites (bony window), the antrostomy was prepared and the remaining bony window was elevated together with the sinus mucosa. At the control sites, the bony window was gently detached before the sinus mucosa elevation and discarded. The space obtained was grafted with deproteinized bovine bone mineral (DBBM). A collagen membrane was positioned on the antrostomy at both sides. The rabbits were euthanized after 2, 4, and 8 weeks in groups of six each. Histologic analyses in different regions of the elevated space were carried out, and a Wilcoxon test was used to estimate differences. Microcomputed tomography (microCT) analyses were also performed. Results: After 2 weeks of healing, higher proportions of new bone were found in the test group compared with the control group due to the higher amount of bone formed in the region subjacent to the sinus mucosa. In this region, higher amounts of new bone were also found in the test group after 4 (P = .028) and 8 weeks of healing (P = .345). After 8 weeks of healing, the percentage of new bone was higher at the control sites compared with the test sites, with the proportions being 25.4% +/- 3.2% and 21.3% +/- 6.1%, respectively. In this period of evaluation, the bony window contributed with 20.1% +/- 5.3% of vital bone in the test group. A fraction of 60.4% +/- 10.8% of its surface was surrounded by new bone. In the microCT analysis, after 8 weeks of healing, fractions of 22.3% +/- 1.6% and 22.2% +/- 0.7% of bone were found in the test and control groups, respectively. Conclusion: The presence of the bony window positively influenced the healing in the elevated space, especially in the submucosa region. The bony window was vital and incorporated into newly formed bone.