Structural and size dependence magnetic properties of Mn-doped NiO nanoparticles prepared by wet chemical method
Journal of Materials Science: Materials in Electronics(2020)
Abstract
Ni1−xMnxO (x = 0.0–0.10) nanoparticles [NPs] were successfully prepared by wet chemical precipitation method at room temperature using polyethylene glycol as a capping agent. The structural, optical, microstructure, and magnetic properties of the prepared NPs were determined by XRD, FTIR, UV.PL SEM, TEM, EDS, and VSM analysis. XRD analysis confirmed the distorting of Mn2+ ions in the NiO lattice with FCC structure. The average crystalline size of undoped and Mn2+ NiO was found to decrease from 39 to 21 nm. Microstructure result shows that the prepared nanoparticles are polycrystalline in nature and the shape of the particles was hexagonal. Optical analysis shows the increase in bandgap from 3.81 to 4.27 eV by strong quantum confinement effect with blue shift in the UV absorption spectra range of 325–290 nm. EDS analysis confirmed that the samples are composed of Ni, Mn, and O without other impurities. FTIR spectra confirmed the formation of Ni–Mn–O stretching frequency. The VSM result suggests that the highest coercivity of about 620 Oe and Mn–Mn super-exchange interaction is responsible for the room-temperature ferromagnetism.
MoreTranslated text
AI Read Science
Must-Reading Tree
Example
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
Generate MRT to find the research sequence of this paper
Chat Paper
Summary is being generated by the instructions you defined