BNL-91263-2010-CP Cryogenic Field Measurement of Pr 2 Fe 14 B Undulator and Performance Enhancement Options at the NSLS-II

Short period (14.5mm) hybrid undulator arrays composed of Praseodymium Iron Boron (Pr2Fe14B) magnets (CR53, NEOMAX, Inc.) and vanadium permendur poles have been fabricated at Brookhaven National Laboratory. Unlike Neodymium Iron Boron (Nd2Fe14B) magnets which exhibit spin reorientation at a temperatures below 150K, PrFeB arrays monotonically increase performance with lower operating temperature. It opens up the possibility for use in operating a cryo-permanent magnet undulator (CPMU) in the range of 40K to 60K where very efficient cryocoolers are available. Magnetic flux density profiles were measured at various temperature ranges from room temperature down to liquid helium (LHe) using the Vertical Testing Facility (VTF) at the National Synchrotron Light Source–II (NSLS-II). Temperature variations of phase error have been characterized. In addition, we examined the use of textured Dysprosium (Dy) poles to replace permendur poles to obtain further improvement in performance.