Comparative study of the shear bond strength of zirconia-based dental ceramics to resin cements after chemo-mechanical surface treatment
semanticscholar(2019)
摘要
Introduction: The loss of retention of zirconia-based fixed partial dentures (FPDs) is one of the most frequently reported failures. Objectives: The purpose of this study was to evaluate the shear bond strength (SBS) of four resin cements to zirconia after air-borne particle abrasion with alumina of different grades and application of respective primers incorporating organophosphate monomers. Material and methods: The 443 cuboid-shape zirconia specimens (Ceramill Zi; Amann Girrbach AG) were divided into 16 research groups, according to the chemo-mechanical modification: air-abrasion with alumina particles of 50 μm, 110 μm or 250 μm grade, no treatment and application of primers and resin cements: Clearfil Ceramic Primer/Panavia F2.0 (Kuraray Medical), Monobond Plus/Multilink Automix (Ivoclar Vivadent AG), AZ-Primer/ResiCem (Shofu), Z-Prime Plus/Duo-Link (Bisco). After storage in 37 ± 1°C distilled water for 24 hours, the SBS test was conducted (Zwick/Roell Z005; Zwick GmbH&Co.KG) at 1 mm/min crosshead speed to failure. Specimens were subjected to fractographic analysis at ×2.5 and ×35 magnification (Seliga Auctus; Seliga Microscopes Sp.z o.o.; SEM S-4700; Hitachi High-Technologies Corporation). Statistical significance was established with the Wilcoxon signed-rank test and the Kruskal-Wallis one-way analysis of variance (p = 0.05). Results: The highest SBS values of zirconia to resin cement were obtained for Z-Prime Plus/DuoLink (8.24-14.15 MPa) and after 50 μm alumina air-abrasion (6.87-14.15 MPa). However, the alumina particle grade was insignificant. A significant decrease in the SBS was observed for untreated specimens (4.60-8.24 MPa). The failure mode in untreated specimens was mainly adhesive, while in sandblasted it was cohesive and mixed. Conclusions: The chemo-mechanical treatment of zirconia surface before adhesive cementation is crucial to obtain satisfactory values of shear bond strength to resin cements.
更多查看译文
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要