Thermal, Mechanical, And Electrical Properties Of Lsco/Mullite Composite Contact Materials For Solid Oxide Fuel Cells

Lanthanum strontium cobaltite (LSCo) is considered as a good candidate cathode contact material for solid oxide fuel cells, due to high electrical conductivity. However, LSCo has a very large coefficient of thermal expansion (CTE) than the cells and metallic interconnects. As a result, poor mechanical stability is expected during thermal cycling. To minimize the CTE mismatch, we investigate a composite approach involving mixing LSCo with an inert material of low CTE, such as mullite at volume fractions from 0.1 to 0.4. Composite's CTE shows a decreasing trend with increasing mullite volume fractions and is consistent with model predictions. X-ray powder diffraction analysis of sintered LSCo/mullite composites exhibits no presence of other phases for samples aged for 500 hours at 800 degrees C, indicating chemical compatibility. Electrical conductivity by a 4-pt method shows a decreasing trend with increasing mullite content. Contact strength of as-sintered and thermally cycled samples show that only the composite with 0.4 volume fraction has a measurable strength; the other composites have no strength. Overall, the composite approach is demonstrated in the LSCo/mullite system to lower the CTE and hence achieve thermal cycle stability. The addition of the inert phase to the LSCo matrix, however, also reduces the electrical conductivity.