Effect of E-44 Epoxy Resin and Pyrolysis Temperature on the Adhesion Strength of SiBCN Ceramic
Journal of Wuhan University of Technology(2020)
摘要
An adhesive of the SiBCN ceramic was synthesized through the polymer derived ceramics (PDC) route. Meanwhile with higher adhesion strength and simpler process condition, the polyborosilazane (PSNB) was modified by E-44 epoxy resin. The E-44 epoxy resin was used to promote the oxidation process of SiBCN, in other words, to produce more amount of SiO 2 -B 2 O 3 glasses. The phase composition, elemental analysis, chemical bonds and microstructure were investigated by using X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and scanning electron microscope (SEM) measurements. The E-44 modified adhesives were cured at 120 °C in air for 2 h, and were pyrolyzed at 1 200, 1 400, and 1 500 °C for 2 h in air, respectively. The highest adhesion strength of the modified adhesive was up to 5.33, 12.23, and 12.50 MPa after being heat treated at 1 200, 1 400, and 1 500 °C, respectively. Finally, we proposed an adhesion model and revealed the adhesion mechanism of SiBCN ceramic.
更多查看译文
关键词
SiBCN ceramic,PDC route,E-44 epoxy resin,pyrolysis temperature,SiO2-B2O3 glasses
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要