Growth of high-quality AlN films on sapphire substrate by introducing voids through growth-mode modification
APPLIED SURFACE SCIENCE(2020)
Abstract
We demonstrate the achieving of high-quality AlN films on flat sapphire substrate (FSS) by introducing voids during growth. Voids are embedded into AlN epilayers through a growth-mode transition from island growth to step flow growth. Such voids significantly facilitated the underlying dislocations annihilation as demonstrated by the transmission electron microscopy (TEM) image. For the 3 mu m-thick AlN film grown on FSS, the full width at half maximum of the X-ray rocking curve was 57/260 arcsec for (0 0 2)/(1 0 2) reflection and a threading dislocation density of 1.7 x 10(8) cm(-2) was determined from plain-view TEM image. Moreover, the voids provided an additional stress relief channel in the AlN film grown on FSS, resulting in a tensile stress comparable to that of grown on nano-patterned sapphire substrate (NPSS). The measured lattice constants and Raman shift of AlN-E-2 (high) peak verified the 3 mu m-thick AlN film grown on FSS is nearly stress free at room temperature. Taking advantages of the deliberately embedded voids, a crack-free and atomically flat AlN film was grown on FSS. The strategy put forward in this work to obtaining high-quality AlN films on FSS is much cost-efficient, which is believed to hold great promise for commercialization in AlN-based devices.
MoreTranslated text
Key words
AlN,Void,Dislocation,Stress relaxation
AI Read Science
Must-Reading Tree
Example
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
Generate MRT to find the research sequence of this paper
Chat Paper
Summary is being generated by the instructions you defined