Enhanced Catalytic Performance of Hierarchical MnOx/ZSM-5 Catalyst for the Low-Temperature NH3-SCR
CATALYSTS(2020)
Abstract
A ZSM-5 zeolite with a hierarchical pore structure was synthesized by the desilication-recrystallization method using tetraethyl ammonium hydroxide (TEAOH) and cetyltrimethylammonium bromide (CTAB) as the desilication and structure-directing agents, respectively. The MnOx/ZSM-5 catalyst was synthesized by the ethanol dispersion method and applied for the low-temperature selective catalytic reduction of NOx with NH3. The results showed that NOx conversion of the hierarchical MnOx/ZSM-5 catalyst could reach 100% at about 120 degrees C and could be maintained in the temperature range of 120-240 degrees C with N-2 selectivity over 90%. Furthermore, the hierarchical MnOx/ZSM-5catalyst presented better SO2 resistance performance than the traditional catalyst in the presence of 100 ppm SO2 at 120 degrees C. XRD, SEM, TEM, XPS, BET, NH3-TPD, and TG were applied to characterize the structural properties of the MnOx/ZSM-5 catalysts. These results showed that the MnOx/ZSM-5 catalyst had micropores (0.78 nm) and mesopores (3.2 nm) leading to a larger specific surface area, which improved the mass transfer of reactants and products while reducing the formation of sulfates. The better catalytic performance over hierarchical MnOx/ZSM-5 catalyst could be attributed to the higher concentration of Mn4+ and chemisorbed oxygen species and higher surface acidity. The improved SO2 resistance was related to the catalyst's hierarchical pore structure.
MoreTranslated text
Key words
hierarchical pore structure,MnOx,ZSM-5,NH3-SCR,SO2 resistance
AI Read Science
Must-Reading Tree
Example
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
Generate MRT to find the research sequence of this paper
Chat Paper
Summary is being generated by the instructions you defined