Engineering Properties Of Lightweight Geopolymer Concrete Using Palm Oil Clinker Aggregate

The palm oil industry generates a significant amount of wastes which their managing has been a major environmental concern in producing countries. The utilization of these wastes as an aggregate source for concrete production will help to sanitize the environment and provides a cheaper and renewable aggregates source for construction industries. This paper presents the results of the experimental program conducted on fly-ash based geopolymer concrete containing Palm Oil Clinker Aggregate (POCA). Several geopolymer concrete mixes were prepared in which POC was used as a replacement to both fine and coarse aggregates at different percentages starting from 25% to 100%. Mix proportioning was done in accordance with ACI 211.1-91. Geopolymer concrete specimens were cast, cured at ambient conditions and tested for the slump, density, water absorption and compressive, shear and flexural strengths. Overall, the use of fly ash-based geopolymer binder and POCA can enhance the sustainability aspects in concrete production as well as produce a high strength concrete. A concrete mixture containing 100% POCA can produce a structural lightweight concrete having a compressive strength of more than 30 MPa and a density of 1821 kg/m(3). The use of a geopolymer binder promotes the workability and strength of POCA concrete and reduces its water absorbability. Incorporation of POCA up to 75% did not much change the structural efficiency of the produced concrete, while it was reduced by 32% when the POCA fully replaced the natural aggregate. Nevertheless, the benefits in terms of cost, energy, and environmental savings cannot be overlooked.