Fabrication of excellent anti-corrosion epoxy coating based on GON-An composites
SURFACE ENGINEERING(2020)
摘要
Polyaniline/graphene oxide (GON-An) composites were synthesized by chemically grafting p-phenylenediamine (PPDA)-modified graphene oxide (GO) with polyaniline (PANI), which was confirmed by FT-IR, XRD, SEM, TEM, Raman spectroscopy, and XPS analyses. The electrochemical impedance spectroscopy test, brine immersion, and Tafel slopes analysis revealed that compared with GO and PPDA-modified GO (GON), GON-An composites which combined the unique corrosion resistance of both PANI and GO exhibited relatively obvious superiority in improving the corrosion resistance of epoxy coating with the same contents. After being immersed in brine for 35 days, the composite epoxy coating containing 1 wt-% of GON-An(1:2) composites in which the mass ratio of GO and PANI was 1:2, possessed a high impedance of 4x10(9) omega cm(2), a high corrosion potential of -0.25 V, and a low corrosion current of 4.119x10(-11) A cm(-2). Furthermore, the anti-corrosive mechanisms of PANI/GO epoxy coatings were discussed.
更多查看译文
关键词
Epoxy coating,graphene oxide,polyaniline,anti-corrosive properties
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要