Recrystallization of biaxially oriented polyethylene film from partially melted state within crystallite networks

POLYMER(2020)

Cited 8|Views18
No score
Abstract
Recrystallization behavior and the final crystallite orientation of biaxially oriented polyethylene (BOPE) film from different melted states have been studied by using differential scanning calorimetry (DSC) and wide-angle X-ray diffraction (WAXD), respectively. WAXD result shows that two kinds of crystallites (1 and 2) with different orientations are aligned around the transverse direction (TD) of the film plane. When BOPE film is annealed in the temperature range of 110 similar to 125 degrees C, the residual crystallites 1 are still aligned along the TD, while the residual crystallites 2 are gradually rotated and aligned along the machine direction (MD). Recrystallization of BOPE film from the partially melted states is enhanced and the maximum crystallization peak shifts to higher temperature by 7 degrees C. The newly formed crystallites after recrystallization are aligned along the TD and MD, respectively. When annealing temperature attains to 128 degrees C, a trace amount of residual crystallites 1 persists along the TD. The newly formed crystallites after recrystallization are also aligned the TD. When the storing temperature range is in 130-150 degrees C, the melt memory effect occurs in BOPE film, and it influences crystallization kinetics and the crystallite orientation.
More
Translated text
Key words
Partially melted state,Orientation,Recrystallization,Biaxially oriented polyethylene (BOPE) film
AI Read Science
Must-Reading Tree
Example
Generate MRT to find the research sequence of this paper
Chat Paper
Summary is being generated by the instructions you defined