Hydrogen-assisted microcrack formation in bearing steels under rolling contact fatigue
International Journal of Fatigue(2020)
Abstract
•H induces voids and cracks at grain boundaries during rolling contact fatigue.•Mixed H embrittlement mechanism: localised plasticity and intergranular debonding.•Quantitative proof of increased void and crack populations upon H ingress.
MoreTranslated text
Key words
Hydrogen embrittlement,Rolling contact fatigue,Crack propagation