Composition-driven inverse-to-conventional transformation of electrocaloric effect and large energy storage density in strontium modified Ba(Zr0.1Ti0.9)O3 thin films
JOURNAL OF MATERIALS CHEMISTRY C(2020)
摘要
In this work, (Ba1-xSrx)Zr0.1Ti0.9O3 (BSZTx, x = 0, 0.15, 0.25 and 0.35) thin films were successfully deposited on La0.7Sr0.3MnO3 (LSMO)-coated (001) SrTiO3 (STO) single crystal substrates using laser molecular beam epitaxy. The BSZTx thin films with compositions of x = 0 and 0.15 display an inverse electrocaloric effect (ECE) with a maximum adiabatic temperature change of Delta T similar to -10 K under 1500 kV cm(-1), while a large positive Delta T amounting to similar to 13 K is discovered in the strontium rich composition, i.e. x = 0.35. For the composition of x = 0.25 where weak ECE (|Delta T| < 2 K) is discovered, an energy storage density of 15.5 J cm(-3) with an efficiency of 69.8% is observed in the temperature range of 303-413 K. The composition-tunable electrocaloric effect and large energy storage density with excellent thermal stability in strontium modified Ba(Zr0.1Ti0.9)O-3 thin films are ascribed to the synergistic effects of different dynamics of polar nano-regions (PNRs) and conformed defect dipoles under large electric fields at elevated temperatures. This work will facilitate the development of novel solid-state cooling devices and provide a design route for high energy storage density devices.
更多查看译文
关键词
electrocaloric effect,strontium,thin films,large energy storage density,composition-driven,inverse-to-conventional
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要