Investigation of Composition Uniformity in Thickness of GaInAsP Layers Grown on InP Substrates by Vapor-Phase Epitaxy
Semiconductors(2019)
摘要
GaInPAs/InP heterostructures grown by metalorganic chemical vapor-phase deposition at a temperature of 600°C and pressure of 0.1 bar are investigated. The thicknesses of the grown GaInAsP layers amount to about 1 μm. For Ga 1 – x In x P 1 – y As y solid solutions with average compositions of x = 0.77–0.87 and y = 0.07–0.42, the variation in the content y of V-group atoms over the epitaxial-layer thickness by a value of Δ y up to 0.1 atomic fractions in the sublattice of the V-group elements is revealed by secondary ion mass spectrometry. In most cases, a change in y occurs in the GaInAsP layer over a length to 200 nm from the InP heterointerface. In certain cases, y varies throughout the entire GaInPAs-layer thickness. For the epitaxial layers with satisfactory crystalline perfection, the value of Δ y is less in the case of better lattice-matching between the GaInPAs epitaxial layer and the substrate. For GaInPAs layers strongly lattice-mismatched with the substrate and characterized by a low degree of crystalline perfection, the value of Δ y is close to zero. All these facts enable us to assume that it is elastic deformations arising in the forming monolayer lattice-mismatched with the growing surface that affect the incorporation of V-group atoms into the forming crystalline lattice.
更多查看译文
关键词
vapor-phase epitaxy,solid solutions,heterostructures,photovoltaic converters
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要