The Tribological Properties Of Bulk Fe2b With Pre-Oxidation Treatment At 750 Degrees C In Air

Purpose The purpose of this study was to investigate the tribological properties of bulk Fe2B with pre-oxidation treatment. Design/methodology/approach Bulk Fe2B was oxidized in an electric box furnace with a soaking time of 9 min under 750 degrees C in air. Then, the tribological experiments were carried out on an UMT-Tribolab tester. Findings The oxide layer was composed of Fe, Fe2O3, Fe3O4, B2O3 and H3BO3. The oxidative direction of bulk Fe2B was perpendicular to the sample surface. But, the oxidative direction of Fe2B crystals was irregular. At 0.1 m/s, the friction coefficient was the lowest. The effects of shortening the running-in period of friction and reducing the friction coefficient by pre-oxidation treatment at 0.1 m/s were remarkable. Nevertheless, the effect of pre-oxidation treatment was futile at 0.2 m/s. Wear mechanisms of oxidized Fe2B mainly were adhesive and abrasive wear. Originality/value The effects of shortening the running-in period of friction and reducing the friction coefficient by pre-oxidation treatment were remarkable.