Non-Destructive Evaluation of Thermally Grown Oxides in Thermal Barrier Coatings Using Impedance Spectroscopy

The growth of thermally grown oxide (TGO) layers in thermal barrier coatings (TBCs) due to the oxidation of the bondcoat alloy is a critical factor affecting the durability of TBCs. In the present study, diverse TBC specimens were subjected to long-term oxidation at various temperatures. The TGO growth mechanism was investigated according to cross-sectional images of the oxidized specimens. Impedance spectroscopy (IS) was performed to measure the electrical properties of the integrated TBCs non-destructively. Considering the influence of the TGO composition, the derived TGO electrical capacitance was found to have a good correspondence to the observed TGO thickness over a wide range 0–18.3 μm, regardless of the diverse specimens and oxidation conditions. The error was less than ±2.0 μm. With a certain design of the electrode size, IS is generalized and is recommended as an accurate and practical non-destructive evaluation method for the determination of TGO thickness within a very wide range in TBC systems under real operating conditions.