3D characterization of the primary Al3Sc phases in an Al-Sc alloy using Synchrotron X-ray tomography and electron microscopy

The three-dimensional structures of the primary Al3Sc particles in an Al-2Sc master alloy were studied by synchrotron X-ray microtomography, scanning and transmission electron microscopy. The Al3Sc phases were found to be a single cube and a cluster of cubes. The surface area, equivalent diameter of the Al3Sc cubes increased with the increasing of cube volume, but the specific surface area decreases. The primary Al3Sc cubes and Al-matrix have the same crystal orientation, indicating that the Al3Sc phases are the heterogeneous nucleation sites for Al. The experimental results show that {\alpha}-Al2O3 are the possible nucleation sites for the Al3Sc cubes.