Magnetoresistance and photoelectrical properties of electron gases at SrTiO 3 (100) surface
JOURNAL OF PHYSICS D-APPLIED PHYSICS(2019)
摘要
Electron gases are created at (100)-oriented SrTiO3 (STO) surfaces by being irradiated with high-speed Ar+ ions. Although fully metallic behavior is observed in both samples, the electron gases at STO surfaces bombarded with acceleration voltage of 200 V (sample L) show smaller carrier density and lower mobility than those at STO surfaces with 400 V acceleration voltage (sample H). Light related magnetoresistance (MR) and magnetic related photoelectrical properties for electron gases at STO surfaces arc compared between sample L and sample H, respectively. Under light illumination, sample L shows increased positive MR, which decreases in sample H. Furthermore, the photoconductivity for sample L becomes slightly smaller and that for sample H rises obviously when the magnetic field is applied. The physical mechanisms responsible for the distinct behavior between the samples have been discussed.
更多查看译文
关键词
magnetoresistance,photoconductivity,electron gas,SrTiO3
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要