Enhanced Reversible Capability Of A Macroporous Znmn2o4/C Microsphere Anode With A Water-Soluble Binder For Long-Life And High-Rate Lithium-Ion Storage

Among the many transition metal oxides, ZnMn2O4 provides relatively high theoretical capacity, low cost, low toxicity, and environmental friendliness for high-performance lithium-ion batteries. However, ZnMn2O4 suffers from limited cycle life, originating from poor electronic conductivity and huge volume change. In this work, ZnMn2O4/C consisting of many carbon layer-coated tiny nanoparticles, forming rough and macroporous microspheres, and microsphere anodes, with water-soluble sodium carboxymethyl cellulose or non-water-soluble poly(vinylidene fluoride), are characterized by electrochemical testing. As a result, the cell with water-soluble sodium carboxymethyl cellulose was shown to exhibit a high reversible capacity of 1249 mA h g(-1) after 100 cycles at a low current density of 200 mA g(-1). Even at a high current density of 500 mA g(-1), it still retains a reversible capacity of 820 mA h g(-1) after 500 cycles with a high coulombic efficiency, thus indicating its long life and high rate.