A new route for preparing Mo-10wt.%Cu composite compacts

In this work, high pure Mo-10 wt% Cu composite powders with a ultrafine particle size are prepared by a two-step reduction process (first carbothermal reduction and then hydrogen reduction). Ammonium heptamolybdate and copper nitrate trihydrate powders are used as molybdenum and copper source, respectively. The mixtures of raw materials are calcined at 400 °C firstly to form the composite oxides which are then reacted with insufficient carbon black at 1050 °C for 2 h. The as-prepared powders are further reduced by hydrogen at 750 °C for 2 h to obtain the ultrafine Mo-10 wt% Cu composite powders. The experimental results show that the residual carbon of the Mo-10 wt% Cu powders can be decreased to 0.015 wt%, and the composite powders have an average particle size of 200 nm. The sintering behavior of ultrafine MoCu powders and the properties (vickers hardness and thermal conductivity) of samples after sintering are investigated. High sintering temperature is beneficial to increase the density of the compact. At 1200 °C, the relative density of the MoCu compacts is 98.8%. The vickers hardness and thermal conductivity of the Mo-10 wt% Cu composites sintered at 1200 °C for 3 h are 233 HV and 130 (W/m·k), respectively.